FSE362 Carbon Fiber Laminate Epoxy

FSE362 Carbon Fiber Laminate Epoxy

Two component epoxy-based adhesive with high bonding strength, shear strength, anti-aging strength. It is used for carbon fiber laminate bonding in CFRP strengthening works..

Contact us
Packaging 15 kg (component A) and 5 kg (component B) per set.
Color Grey, White. Mixture: light grey.
Shelf Life 18 months in original, unopened packaging. Store dry at temperatures between 4 and 32 °C.
Mix Ratio A:B = 3:1 by weight
Service Temperatures +5 °C min. / +40°C max.
Operable time 150 minutes(10°C); 50 minutes(23°C); 40 minutes(30°C)
Consumption 3-4 kg/sqm
Thixotropic Index 4.0 min.
Sagging Mobility (25°C) 2.0 max.
Density after Curing 1.4 g/cm³
Tensile Strength(ASTM D638) 62 Mpa
Tensile Modulus (ASTM D638) 8000 Mpa
Elongation at Break(ASTM D638) 2.07 %
Compressive Strength (ASTM D695) 117 Mpa
Flexural Strength(ASTM D790) 115 Mpa
Shear Strength (ASTM D732) 56 Mpa
Bonding Strength (ASTM C882) 40 Mpa
Deflection Temperature (ASTM D648) 65 °C
Water Absorption (ASTM D470) 0.06 %
Wet and Heat Ageing shear strength decrease rate: 12% max.
Heat Aging Resistance same temperature, 10 minutes, shear strength decrease rate: 5% max.,
Freezing and Thawing shear strength decrease rate: 5% max.
Fatigue Stress 2×10 6 times continuous sine wave fatigue loads, no specimen destroy.
Stress Resistance no steel - steel tensile shear specimens destroy; creep deformation value: 0.4 mm max.
Salt Resistance no cracks or come unglued; strength decrease rate: 5% max.
Alkaline Resistance no strength decrease; as the concrete damage, no cracks or come unglued.
Acid Resistance as the concrete damage, no cracks or degumming.

 

Related Products

新闻动态

  • 22 2020-02
    How to do structural strengthening with carbon fiber

    Carbon fiber reinforcement is a new type of reinforcement method that plays a very important role in building reinforcement engineering. There are many places where it can be used. In the building reinforcement industry, carbon fiber reinforcement is…

  • 15 2020-02
    Gaoziku Reservoir Reinforcement Engineering Campaign Announcement

    This campaign project Gaoziku Reservoir Reinforcement Project (project name) has been organized and implemented by Suining Kaida Investment Co., Ltd. as the project owner according to the approval of the management committee. The project has been qua…

  • 18 2019-12
    The most comprehensive strategy of Concrete column reinforcement

    Concrete column is the main load-bearing component in the building. With the increase of the service time of the building, the durability of the concrete column is prone to decline and the strength and rigidity are insufficient due to the early defec…

  • 18 2019-12
    New Material of Composite Piling

    Composite sheet pile is a kind of high-strength new material, which is made of the environmental polymer reinforced composite material by a variety of additives. The shape of sheet pile is designed according to the mechanical principle, adopting the …

  • 16 2019-12
    Stair design and reinforcement

    Stairs are divided into two types: staircases and beams. Slab stairs are composed of platform beams, platform slabs, and ramp slabs. Beam staircases have increased ramp sloping beams compared to slab stairs. The stair steps and plates have similar st…

  • 10 2019-12
    Decrypting Carbon Fiber

    Carbon fiber is made of organic parent fiber such as polyacrylonitrile (PAN) (or asphalt, viscose) by pyrolysis method under high temperature above 1000 degrees Celsius inert gas (the result is to remove most elements except carbon) Is an inorganic p…