FSFIX450 Anchoring Epoxy

Reliable Quality

In compliance with the most strict standards, passed a number of performance test, no crystallizing and sagging.

Focus on High-Quality

Fatigue Testing of 2 Million Times
Testing of harsh environments( 90 days’ moisture and heat aging resistance, -25 ℃ to 35 ℃ freeaing and thawing temprature) gurantee high quality, 50 years’ serving life.
Packaging 450ml side-by-side 2:1
Color Component A: white, Component B: grey/ red

Component A+B mixed: grey /pink

Customized colors are available

Shelf Life 18 months if stored properly in original and unopened packaging, in cool and dry conditions, out of direct sunlight, and at temperatures between 5 and 25 °C (41 and 77 °F). Pre-condition product to 23 °C (73 °F) to ease application when using hand dispensers and working at low temperatures.
Mix Ratio A:B = 5:1 by volume
Service Temperatures -40 °C min. / +50 °C max.
Viscosity of Mixture 18 pa·s
Density after curing 1.5 g/cm³
Tensile Strength (ASTM D638) 55 Mpa min.
Tensile Modulus (ASTM D638) 3500 Mpa min.
Elongation (ASTM D638) 1.7 % min.
Flexural Strength (ASTM D790) 75 Mpa min.
Compressive Strength(ASTM D695) 100 Mpa min.
Thixotropy Index 4.2 min.
Sagging Mobility (25°C) 1.4mm max.
Distortion Temperature 66 °C min.
Steel-Steel Tensile Anti-shear Strength 16 Mpa min.
Steel-Steel Tensile Anti-shear Strength 16 Mpa min.
Under the constraint drawing condition, ribbed steel bars and C30, Φ25, L=150mm Tensile Strength 11 Mpa min.
Boding Strength with Concrete C60, Φ25, L=125mm 18Mpa min.
Steel-steel T Impact Stripping Length 25mm max.
Non-volatile Matter Content (solid content) 99.5 % min.


Wet and Heat Ageing shear strength decrease rate: 8 % max..
Heat Aging Resistance shear strength decrease rate: 4.7 % max..
Freezing and Thawing shear strength decrease rate: 3.8 % max..
Fatigue Stress 2×10 6 times continuous sine wave fatigue loads,

no specimen destroys.

Stress Resistance no steel - steel tensile shear specimens destroy,

creep deformation value: 0.1 mm max..

Salt Resistance strength decrease rate: 4.3 % max., no cracks or come unglued.
Alkaline Resistance no strength decrease;

as the concrete damage, no cracks or come unglued.

Acid Resistance concrete damage, no cracks or degumming.


  • 22 2020-02
    How to do structural strengthening with carbon fiber

    Carbon fiber reinforcement is a new type of reinforcement method that plays a very important role in building reinforcement engineering. There are many places where it can be used. In the building reinforcement industry, carbon fiber reinforcement is…

  • 15 2020-02
    Gaoziku Reservoir Reinforcement Engineering Campaign Announcement

    This campaign project Gaoziku Reservoir Reinforcement Project (project name) has been organized and implemented by Suining Kaida Investment Co., Ltd. as the project owner according to the approval of the management committee. The project has been qua…

  • 18 2019-12
    The most comprehensive strategy of Concrete column reinforcement

    Concrete column is the main load-bearing component in the building. With the increase of the service time of the building, the durability of the concrete column is prone to decline and the strength and rigidity are insufficient due to the early defec…

  • 18 2019-12
    New Material of Composite Piling

    Composite sheet pile is a kind of high-strength new material, which is made of the environmental polymer reinforced composite material by a variety of additives. The shape of sheet pile is designed according to the mechanical principle, adopting the …

  • 16 2019-12
    Stair design and reinforcement

    Stairs are divided into two types: staircases and beams. Slab stairs are composed of platform beams, platform slabs, and ramp slabs. Beam staircases have increased ramp sloping beams compared to slab stairs. The stair steps and plates have similar st…

  • 10 2019-12
    Decrypting Carbon Fiber

    Carbon fiber is made of organic parent fiber such as polyacrylonitrile (PAN) (or asphalt, viscose) by pyrolysis method under high temperature above 1000 degrees Celsius inert gas (the result is to remove most elements except carbon) Is an inorganic p…