FSE 322 Impregnating Epoxy

HIGH MODULUS, HIGH STRENGTH,
IMPREGNATING ADHESIVE FOR THE CFRP(fabric) SYSTEM

Low viscosity, good impregnation, with certain thixotrpic property, used for impregnation and paste of reinforced component surface and fiber products, it an impregnating adhesive in CFRP system

◆Long pot life and open time.
◆Tolerant of moisture before, during and after cure.
◆High strength, high modulus adhesive.
◆Excellent adhesion to concrete, masonry, metals, wood and most structural materials.
◆Fully compatible and developed specifically for the FS Wrap System.
◆High creep resistance under permanent load.
◆High abrasion and shock resistance.
◆Solvent-free, VOC-compliant.
◆High temperature resistance.

Packaging 20 kg (component A) and 10 kg (component B) per set, smaller package is available
Color Light yellow
Shelf Life 18 months in original, unopened packaging. Store dry at temperatures between 4 and 32 °C.
Mix Ratio A:B = 2:1 by weight
Service Temperatures +5 °C min. / +40°C max.
Operable time 70 minutes
Tacky Dry Time (25°C) 1.5 hours
Curing Time (25°C) 3~7 days
Tensile Strength (ASTM D638) 60 MPa
Tensile Elastic Modulus (ASTM D638) 3100 Mpa
Compressive Strength (ASTM D695) 95 MPa
Elongation at Break(ASTM D638) 6%
Flexural Strength(ASTM D790) 240 MPa
Steel-steel Adhesive Tensile Strength 40 Mpa min.
Steel-steel Tensile Shear Strength 14 Mpa min.
Steel - steel T Impact stripping length 20mm max.
Pulling Bonding Strength along with Concrete 2.5 Mpa min.
Steel-concrete Tensile C60 concrete damage

Related Products

新闻动态

  • 22 2020-02
    How to do structural strengthening with carbon fiber

    Carbon fiber reinforcement is a new type of reinforcement method that plays a very important role in building reinforcement engineering. There are many places where it can be used. In the building reinforcement industry, carbon fiber reinforcement is…

  • 15 2020-02
    Gaoziku Reservoir Reinforcement Engineering Campaign Announcement

    This campaign project Gaoziku Reservoir Reinforcement Project (project name) has been organized and implemented by Suining Kaida Investment Co., Ltd. as the project owner according to the approval of the management committee. The project has been qua…

  • 18 2019-12
    The most comprehensive strategy of Concrete column reinforcement

    Concrete column is the main load-bearing component in the building. With the increase of the service time of the building, the durability of the concrete column is prone to decline and the strength and rigidity are insufficient due to the early defec…

  • 18 2019-12
    New Material of Composite Piling

    Composite sheet pile is a kind of high-strength new material, which is made of the environmental polymer reinforced composite material by a variety of additives. The shape of sheet pile is designed according to the mechanical principle, adopting the …

  • 16 2019-12
    Stair design and reinforcement

    Stairs are divided into two types: staircases and beams. Slab stairs are composed of platform beams, platform slabs, and ramp slabs. Beam staircases have increased ramp sloping beams compared to slab stairs. The stair steps and plates have similar st…

  • 10 2019-12
    Decrypting Carbon Fiber

    Carbon fiber is made of organic parent fiber such as polyacrylonitrile (PAN) (or asphalt, viscose) by pyrolysis method under high temperature above 1000 degrees Celsius inert gas (the result is to remove most elements except carbon) Is an inorganic p…