Two-component epoxy resin for saturating carbon fiber fabric in lay-up applications.
Two-component, solvent-free epoxy resin engineered for saturating and bonding carbon fibre fabrics to concrete, masonry, steel, and timber substrates. The thixotropic formula enables vertical and overhead application without sagging, while its long 70-minute pot life allows comfortable working. Colour-coded, VOC-compliant components ensure correct mixing, and the moisture-tolerant formulation delivers reliable performance even on damp substrates.
| Property | Value |
|---|---|
| Appearance (Mixed) | Light yellow |
| Mix Ratio | A:B = 2:1 by weight |
| Packaging | 20 kg (A) + 10 kg (B) per kit |
| Pot Life (23°C) | 70 min |
| Touch-Dry Time | 1.5 h |
| Full Cure | 7 days |
| Service Temperature | −5°C to +40°C |
| Thixotropic Index | ≥ 3.0 |
| Non-volatile Content | ≥ 99.5% |
| Tensile Strength (ASTM D638) | 55 MPa |
| Tensile Elastic Modulus | 3.1 GPa |
| Elongation | 2.3% |
| Flexural Strength | 80 MPa |
| Compressive Strength | 90 MPa |
| Steel-to-Steel Tensile | ≥ 40 MPa |
| Steel-to-Steel Shear (ASTM D1002) | ≥ 14 MPa |
| Bond to Concrete (ASTM C882) | ≥ 2.5 MPa (concrete failure) |
| Consumption (200 g/m² fabric) | 0.5–0.7 kg/m² per layer |