雙組分環氧樹脂，用於溼法貼敷碳纖維布的浸漬。
雙組份、無溶劑環氧樹脂，專為含浸並黏結碳纖維布至混凝土、磚石、鋼材及木材基材而設計。觸變配方可進行垂直與仰面施工而不垂流，70 分鐘長可操作時間提供從容施作。色碼區分、符合 VOC 規範的組份確保正確混合，且耐濕配方在潮濕基材上仍能提供可靠性能。
| 性能 | 數值 |
|---|---|
| Appearance (Mixed) | Light yellow |
| Mix Ratio | A:B = 2:1 by weight |
| Packaging | 20 kg (A) + 10 kg (B) per kit |
| Pot Life (23°C) | 70 min |
| Touch-Dry Time | 1.5 h |
| Full Cure | 7 days |
| Service Temperature | −5°C to +40°C |
| Thixotropic Index | ≥ 3.0 |
| Non-volatile Content | ≥ 99.5% |
| Tensile Strength (ASTM D638) | 55 MPa |
| Tensile Elastic Modulus | 3.1 GPa |
| Elongation | 2.3% |
| Flexural Strength | 80 MPa |
| Compressive Strength | 90 MPa |
| Steel-to-Steel Tensile | ≥ 40 MPa |
| Steel-to-Steel Shear (ASTM D1002) | ≥ 14 MPa |
| Bond to Concrete (ASTM C882) | ≥ 2.5 MPa (concrete failure) |
| Consumption (200 g/m² fabric) | 0.5–0.7 kg/m² per layer |