Ultra-high-strength PBO mesh for FRCM systems with exceptional ductility and fire resistance.
High-strength PBO (polybenzoxazole) fibre mesh for FRCM structural strengthening. Combined with FMM inorganic mortar, FPM88 forms an inorganic-matrix composite with exceptional tensile capacity, ductility, and durability — without the fire and thermal limitations of epoxy systems. PBO fibre delivers 5,800 MPa tensile strength and 270 GPa stiffness, superior to aramid and comparable to high-modulus carbon fibre.
| 특성 | 값 |
|---|---|
| PBO Fibre Tensile Strength | 5,800 MPa |
| PBO Fibre Elastic Modulus | 270 GPa |
| Elongation | 2.5% |
| Fibre Density | 1.56 g/cm³ |
| Decomposition Temperature | 650°C |
| Areal Weight (Warp) | 88 g/m² |
| Nominal Thickness (Warp) | 0.056 mm |
| Dry Mesh Tensile Elastic Modulus | 190 GPa |
| Ultimate Tensile Strength (FRCM) | 2,780 MPa |
| Ultimate Tensile Strength (Dry Fabric) | 3,280 MPa |
| Standard | CNR-DT215/2018 |
| Colour | Gold yellow |
| Orientation | Unidirectional (0°) |
| Width | 100 cm (uni: 25 cm) or customised |
| Roll Length | 20 m / roll |
| Compatible With | FMM mortar, FCA 10/450 anchor |